Designation: A 1010/A 1010M – 01
e1
Standard Specification for
Higher-Strength Martensitic Stainless Steel Plate, Sheet, and
Strip
1
This standard is issued under the fixed designation A 1010/A 1010M; the number immediately following the designation indicates the
year of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last
reapproval. A superscript epsilon (e) indicates an editorial change since the last revision or reapproval.
e
1
NOTE—Editorial changes were made in August 2001.
1. Scope
1.1 This specification covers martensitic stainless steels for
various structural, architectural, pressure vessel, and heat-
resisting applications. The mechanical properties of these
steels are customarily, but not necessarily, developed by a
suitable heat treatment generally referred to as tempering.
1.2 Steel products under this specification are available in
two grades:
Grade Yield Strength, min, ksi [MPa]
40 [275] 40 [275]
50 [350] 50 [350]
1.3 The maximum thickness of plates is limited only by the
capacity of the composition to meet the specified mechanical
property requirements; however, current practice normally
limits the maximum thickness of plates furnished under this
specification to 1 in. [25 mm].
1.4 The values stated in inch-pound or SI units are to be
regarded separately as the standard. Within the text, SI units are
shown in brackets. The values stated in each system are not
exact equivalents; therefore, each system must be used inde-
pendently of the other. Combining values from the two systems
may result in nonconformance with the specification. The
inch-pound units shall apply unless the “M” designation of this
specification is specified in the purchase order.
2. Referenced Documents
2.1 ASTM Standards:
A 480/A 480M Specification for General Requirements for
Flat-Rolled Stainless and Heat-Resisting Steel Plate,
Sheet, and Strip
2
A 673/A 673M Specification for Sampling Procedure for
Impact Testing of Structural Steel
3
E 527 Practice for Numbering Metals and Alloys (UNS)
4
2.2 Other Document:
SAE J1086 Recommended Practice for Numbering Metals
and Alloys
5
3. General Requirements
3.1 The following requirements for orders for material
furnished under this specification shall conform to the appli-
cable requirements of the current edition of Specification
A 480/A 480M.
3.1.1 Terminology,
3.1.2 Ordering Information,
3.1.3 Process,
3.1.4 Heat Analysis,
3.1.5 Product Analysis,
3.1.6 Finish for Sheet,
3.1.7 Finish for Strip,
3.1.8 Finish for Plates,
3.1.9 Test Specimens,
3.1.10 Number of Tests,
3.1.11 Test Methods,
3.1.12 Retests and Retreatment,
3.1.13 Dimensions and Permissible Variations,
3.1.14 Workmanship,
3.1.15 Packaging, Marking, and Loading,
3.1.16 Inspection,
3.1.17 Rejection and Rehearing, and
3.1.18 Material Test Report and Certification.
4. Chemical Composition
4.1 The steel shall conform to the requirements as to
chemical composition specified in Table 1, and shall conform
to applicable requirements specified in the current edition of
Specification A 480/A 480M.
5. Heat Treatment
5.1 The material shall be heat-treated by tempering to meet
the requirements of this specification. The tempering tempera-
ture shall not exceed 1400°F [760°C]. Prior to tempering, the
steel shall be in the as-rolled, normalized or quenched condi-
tion.
1
This specification is under the jurisdiction of ASTM Committee A01 on Steel,
Stainless Steel, and Related Alloys and is the direct responsibility of Subcommittee
A01.17 on Flat-Rolled and Wrought Stainless Steel.
Current edition approved Mar. 10, 2001. Published April 2001. Originally
published as A 1010-00. Last previous edition A 1010-00.
2
Annual Book of ASTM Standards, Vol 01.03.
3
Annual Book of ASTM Standards, Vol 01.04.
4
Annual Book of ASTM Standards, Vol 01.01.
5
Available from Society of Automotive Engineers, 400 Commonwealth Drive,
Warrendale, PA 15096.
1
Copyright © ASTM, 100 Barr Harbor Drive, West Conshohocken, PA 19428-2959, United States.
Copyright ASTM International
Provided by IHS under license with ASTM
Not for Resale
No reproduction or networking permitted without license from IHS
--`-`-`,,`,,`,`,,`---
资源评论
std86021
- 粉丝: 92
- 资源: 2567
最新资源
- 基于Python实现对书旗小说网进行逆向，实现整本书的采集源代码 并使用tkinter做了GUI界面
- 基于Python实现对塔读小说的免费内容进行整本书的采集源代码，利用JS逆向对每章节中的文字广告进行去除
- Java将2个List集合合并到一个List里面并排序工具类
- 1123231321321321
- 基于Python的歌曲搜索播放器源代码，利用requests库对歌曲宝网站进行歌曲采集，并用tkinter做了UI
- kernel-devel-3.10.0-1062.21.1.el7.x86-64.rpm
- kernel-3.10.0-1062.21.1.el7.x86-64.rpm
- A2_smvs.zip
- Assignment2(4).ipynb
- 用pytorch框架实现的油井时间序列动态预测的模型，其中包含一些传统的时间序列预测方法 .zip
资源上传下载、课程学习等过程中有任何疑问或建议，欢迎提出宝贵意见哦~我们会及时处理！
点击此处反馈