第 19 卷第 3 期 中国有色金属学报 2009 年 3 月
Vol.19 No.3 The Chinese Journal of Nonferrous Metals Mar. 2009
文章编号：1004-0609(2009)03-0595-06
表面活性剂对超细银粉分散性能的影响
魏丽丽
1
，徐盛明
1, 2
，徐 刚
1
，陈崧哲
1
，李林艳
1
(1. 清华大学 核能与新能源技术研究院，北京 100084；
2. 中南大学 粉末冶金国家重点实验室，410082)
摘 要：在以抗坏血酸为还原剂、银氨配合物为前驱体、PVP 为保护剂及表面活性剂为分散剂的液相化学还原体
系中制备超细银粉，研究阳离子、阴离子和非离子表面活性剂在银粉制备过程中的防团聚作用和分散作用，并采
用扫描电镜(SEM)和 X 射线衍射等对还原产物进行形貌观察和结构表征。结果表明：表面活性剂的种类对制备样
品的纯度、分散性和颗粒大小有着重要的影响，其中阳离子表面活性剂和阴离子表面活性剂的分散效果不明显，
非离子表面活性剂的分散效果最好。对吐温(TW)系列分散剂的研究表明：TW 相对分子质量的大小对银粉颗粒的
分散效果、形貌和大小也有显著影响；采用 TW80 分散剂可制备出高分散、窄粒级的超细银粉。
关键词：超细银粉；表面活性剂；抗团聚；分散
中图分类号：TG 146.32; TB383; TF 832 文献标识码： A
Effects of surfactants on dispersive performance of
ultrafine silver powder
WEI Li-li
1
, XU Sheng-ming
1, 2
, XU Gang
1
, CHEN Song-zhe
1
, LI Lin-yan
1
(1. Institute of Nuclear and New Energy Technology, Tsinghua University, Beijing 100084, China;
2. State Key Laboratory of Powder Metallurgy, Central South University, Changsha 410083, China)
Abstract: The preparation of ultrafine silver powder was investigated by reducing Ag(NH
3
)
2+
with ascorbic acid in the
presence of poly-(vinylpyrrolidone) (PVP) as protective agent and surfactants as dispersant. The effects of cation, anion,
and non-ion surfactants on aggregation-proof and dispersion of silver particles in the preparing silver powder were
investigated, and the pattern and phase of reducing products were also characterized by scanning electron microscopy
(SEM) and X-ray diffractometry (XRD). The results show that the surfactant species impact apparently on the purity,
dispersion degree and particle size of the reducing sample. The non-ion surfactants can improve the dissemination of
ultrafine silver particles, but both the dispersive effects of cation and anion surfactants are unapparent. Moreover, the
results of reducing experiments with a series of TW surfactants show that the relative molecular mass of TW affects the
dissemination, pattern and size of silver particles, and the well-dispersed ultrafine silver powder with narrow size
distribution can be prepared in the presence of TW 80 surfactant.
Key words: ultrafine silver powder; surfactant; aggregation-proof; dispersion
超细银粉除具有普通银粉在电、热、磁等方面的
优良性能外，还具有一般超细粉体的性质，即粉体粒
径小、比表面积大、表面剩余电荷多、表面张力大、
单位比表能高等。然而，这些超细粒子的性质使单个
超细粒子在热力学上往往处于不稳定状态，导致超细
粒子间的自发相互吸引与凝聚，且团聚现象在粒子的
制备及后处理的每一步操作过程中都极易发生，而超
细粒子以团聚体形式存在时则导致了粒子粒径增大、
基金项目：国家自然科学基金资助项目(50274045；50674060)；中南大学粉末冶金国家重点实验室开放基金资助项目(2007)
收稿日期：2008-03-08；修订日期：2008-09-03
通讯作者：徐盛明，副教授，博士；电话：010-89796082；传真：010-62773585；E-mail: smxu@tsinghua.edu.cn
资源评论